上海高高興晟特鋼集團有限公司專業、專注量身打造50Mn18Cr4WN無磁護環鋼：?

50Mn18Cr4WN圓鋼?50Mn18Cr4WN鋼板

50Mn18Cr4WN扁鋼?50Mn18Cr4WN鍛件??

50Mn18Cr4WN環件?50Mn18Cr4WN方鋼?

50Mn18Cr4WN?Φ10(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ12(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ15(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ20(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ25(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ30(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ35(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ40(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ50(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ60(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ70(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ80(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ90(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ100(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ110(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ120(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ130(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ140(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ150(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ160(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ170(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ180(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ190(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ200(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ210(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ220(MM)??無磁護環鋼?

50Mn18Cr4WN?Φ230(MM)??無磁護環鋼?

——————————?

上海高高興晟特鋼集團有限公司 ??

電話：18917081101? ??

微信：18917081101 ????

QQ：404914802 ?

聯系人：粟太成?

電子郵件：404914802@qq.com?

地址：上海市寶山區撫遠路1288

—————————————?

牌號：50Mn18Cr4WN?

材料類別：奧氏體無磁鋼?

執行標準：1268-1993?

特性及適用范圍： 50Mn18Cr4WN奧氏體無磁鋼的基礎上加鎢、氮得到。鎢使鋼中碳化物沉淀較慢，氮擴大和穩定奧氏體，使鋼進一步強化；固溶處理后，進行半熱變形強化或冷變形強化，以滿足不同強度要求。用于汽輪發電機無磁性護環鍛件及其他要求無磁性的零部件。?

50Mn18Cr4WN化學成分：?

碳?C?：0.40～0.60；?

硅?Si：0.30～0.80；?

錳?Mn：17.00～19.00；?

硫?S?：≤0.025；?

磷?P?：≤0.080；?

鉻?Cr：3.00～5.00；?

氮?N?：0.08～0.12；?

鎢?W?：0.70～1.20。?

50Mn18Cr4WN力學性能：?

抗拉強度?σb?(MPa)：I級,≥895；??

條件屈服強度?σ0.2?(MPa)：I級,≥760；?

伸長率?δ5?(％)：I級,≥25；?

斷面收縮率?ψ?(％)：I級,≥35。?

熱處理規范及金相組織：?

50Mn18Cr4WN熱處理規范：?

1)熱成形后和變形強化前固溶處理;?

2)變形強化后以≤40℃h的速率,加熱到320～350℃,保溫8～12h,以≤40℃h速率緩冷至100℃以下,以消除殘余應力. 上海高高興晟特鋼集團有限公司真實信息、真格品質、真實價格提供50Mn18Cr4WN無磁護環鋼。?

?