| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 基本性能 | 熔體流動速率 | 230℃/3.8kg | ASTM D-1238 | 3.3 | g/10min |
| 物理性能 | 比重 | ASTM D-792 | 1.19 | g/cm3 | |
| 模具收縮率 | Flow,3.20mm | ASTM D-955 | 0.50-0.70 | % | |
| 機械性能 | 拉伸模量 | ASTM D-638 | 2070 | MPa | |
| 拉伸屈服強度 | ASTM D-638 | 37.8 | MPa | ||
| 拉伸斷裂強度 | ASTM D-638 | 30.3 | MPa | ||
| 拉伸屈服伸長率 | ASTM D-638 | 2.4 | % | ||
| 拉伸斷裂伸長率 | ASTM D-638 | 17 | % | ||
| 彎曲模量 | 50.0mm Span | ASTM D-790 | 2340 | MPa | |
| 彎曲屈服強度 | 50.0mm Span | ASTM D-790 | 67.6 | MPa | |
| IZOD缺口沖擊強度 | 23℃ | ASTM D-256 | 214 | J/m | |
| 電氣性能 | 體積電阻率 | IEC 60093 | >1.0E+14 | ohm.cm | |
| 介電強度 | 3.20mm,in Oil | IEC 60243-1 | 20.00 | KV/mm | |
| 熱性能 | 熱變形溫度 | 0.45MPa，未退火，3.20mm | ASTM D-648 | 86.1 | ℃ |
| 熱變形溫度 | 1.80MPa，未退火，3.20mm | ASTM D-648 | 75.0 | ℃ | |
| 維卡軟化溫度 | ASTM D-1525 | 93.9 | ℃ | ||
| CLTE | Flow,-40TO40℃ | ASTM E-831 | 0.000090 | cm/cm/℃ | |
| CLTE | Transverse,-40TO40℃ | ASTM E-831 | 0.000092 | cm/cm/℃ | |
| 燃燒性 | 1.50mm | UL 94 | V-0 | ||
| 燃燒性 | 2.79mm | UL 94 | 5VA | ||
免責聲明：當前頁為 現貨供應ABS 美國GE FR15U 阻燃耐候性產品信息展示頁，該頁所展示的 現貨供應ABS 美國GE FR15U 阻燃耐候性產品信息及價格等相關信息均有企業自行發布與提供， 現貨供應ABS 美國GE FR15U 阻燃耐候性產品真實性、準確性、合法性由店鋪所有企業完全負責。世界工廠網對此不承擔任何保證責任，亦不涉及用戶間因交易而產生的法律關系及法律糾紛，糾紛由會員自行協商解決。
友情提醒：世界工廠網僅作為用戶尋找交易對象，就貨物和服務的交易進行協商，以及獲取各類與貿易相關的服務信息的渠道。為避免產生購買風險，建議您在購買相關產品前務必確認供應商資質及產品質量。過低的價格、夸張的描述、私人銀行賬戶等都有可能是虛假信息，請您謹慎對待，謹防欺詐，對于任何付款行為請您慎重抉擇。
投訴方式：fawu@gongchang.com是處理侵權投訴的專用郵箱，在您的合法權益受到侵害時，請將您真實身份信息及受到侵權的初步證據發送到該郵箱，我們會在5個工作日內給您答復，感謝您對世界工廠網的關注與支持！
(c)2008-2025 世界工廠網V3.6 All Rights Reserved 豫ICP備2024066506號